Processes, Vol. 13, Pages 1000: Bacterial-Retted Hemp Fiber/PLA Composites

Processes doi: 10.3390/pr13041000

Authors:
Lee M. Smith
Yu Fu
Raj Kumar Pittala
Xun Wang
Chloe Jabel
Kelvin Masignag
Josue Arellanes
Mahan Ghosh
Sheldon Q. Shi
Melanie Ecker
Cuicui Wang

The push for sustainability in all facets of manufacturing has led to an increased interest in biomass as an alternative to non-renewable materials. Hemp bast fiber mats were produced from a bacterial retting process, named BFM, as the fiber reinforcement. The objective of this study was to evaluate the feasibility of laminating BFM with polylactic acid (PLA) for a composite panel product. Since both BFM and PLA are biodegradable, the resulting BFM-PLA composites will be 100% biodegradable. PLA pallets were processed into thin polymer sheets which served as the matrix. The BFM and PLA plates were laminated in five layers and compression-molded into composite panels. Experiments were conducted on the three BFM-to-PLA ratios (35/65, 45/55, and 50/50). Mechanical properties (tensile and bending properties) and physical properties (thickness swell and water absorption) were tested and compared to the currently commercial sheet molding compound (SMC) from fiber glass. The thermal behavior of the BFM/PLA composites was characterized using dynamic mechanical analysis (DMA) and differential scanning calorimetry (DSC). The developed BFM/PLA composite product is a sustainable alternative to existing synthetical fiber-reinforced polymer (FRP) that is biodegradable in landfill at the end of life.

Source link

Lee M. Smith www.mdpi.com